Oxidation of thiophene over copper-manganese mixed oxides

Szynkowska, Małgorzata I., Węglińska, Aneta, Wojciechowska, Elżbieta and Paryjczak, Tadeusz Oxidation of thiophene over copper-manganese mixed oxides Chemical Papers, Vol.63, No. 2, 2009, 233-238

Document type: Článok z časopisu / Journal Article
Collection: Chemical papers  

Author(s) Szynkowska, Małgorzata I.
Węglińska, Aneta
Wojciechowska, Elżbieta
Paryjczak, Tadeusz
Title Oxidation of thiophene over copper-manganese mixed oxides
Journal name Chemical Papers
Publication date 2009
Year available 2009
Volume number 63
Issue number 2
ISSN 0366-6352
Start page 233
End page 238
Place of publication Poland
Publisher Versita
Collection year 2009
Language english
Subject 290000 Engineering and Technology
291100 Environmental Engineering
Abstract/Summary Commercial hopcalite calcined at different temperatures and hopcalite modified with noble metals (Pt, Pd, and Au) were studied in oxidation of thiophene. Surface and bulk properties of catalysts were studied using temperature-programmed reduction (TPRH2), X-ray diffraction method (XRD) and thermal analysis (TG-DTA-MS). It was shown that calcined samples displayed higher activity in comparison with commercial untreated hopcalite; however, a lower temperature of calcination was favourable. High temperature of thermal treatment induced an increase in the crystallinity and a decrease in the surface area of the samples, and, as a consequence, the loss of catalysts activity. Moreover, marked improvement in the catalytic performance of platinum and palladium modified catalysts in relation to base hopcalite was observed. The obtained results indicate that the higher activity of samples containing Pt and Pd was accompanied by better reducibility of the catalysts.
 
Related Links
Link Description
http://www.springerlink.com/content/c30g8964868012g5/?p=2d98bb179b194ab28a2a9...   fulltext  
 
 
User Comments
 
Access Statistics: 0 Abstract Views Detailed Statistics
Created: Fri, 19 Mar 2010, 12:07:04 CET by Jana Taptičová . Detailed History